Base material Print
Layer material
 StandardWith overhead expenses
Material typeFR4 (Tg 135 °C)FR4 (Tg 150°C), FR4 (Tg 170 °C)
Thickness without the  basic copper 0.20mm; 0.25mm; 0.36mm; 0.51mm; 0.76mm; 1.00mm0.30mm; 0.41mm; 0.61mm
Basic copper18µm; 35µm70µm; 105µm
Thickness tolerance inc. basic copperMIL-S-13949H tolerance, last edition, grade IIIPC 4101A grade B 
Material characteristics

Permittivity er at 1MHz                                4.6 - 4.9

Dielectric loss tand at 1MHz                        0.019

Resistance to current leakage CTI                200 degree

Electrical strength (min.)                             39kV/mm

Fire-retardant class                                     UL 94V-0

Prepreg
 StandardWith overhead expenses
Material typeFR4 (Tg 135 °C)FR4 (Tg 150°C), FR4 (Tg 170 °C)
Prepreg type1080; 2116; 7628 
Material thickness63µm; 110µm; 180µm 
Material characteristics

Permittivity er at 1MHz                                      4.6 - 4.9

Dielectric loss tand at 1MHz                              0.019

Resistance to current leakage CTI                      200 degree

Electrical strength (min.)                                   39kV/mm

Fire-retardant class                                           UL 94V-0

Min. final copper depending on basic copper and PCB thickness
Final copper /basic copper/ - PCB thickness

43µm / 18µm / 0.8 ÷ 2.0mm

60µm / 35µm / 0.8 ÷ 3.2mm

95µm / 70µm / 0.8 ÷ 2.0mm

130µm / 105µm / 0.8 ÷ 2.0mm

130µm / 105µm / 2.1 ÷ 3.2mm

Tolerance±10%±10%
 